Polyamide 6 Relative Viscosity Value: 2.45; Spinning Grade Polyamide 6; Chinese Polyamide 6; Low Viscosity Polyamide 6; Nylon6;

• CAS No.: 25038-54-4
• Formula: C6h13no
• Material: Polyamide(Nylon 6.66)/PA
• Usage: Engineering Plastics
• Plastic Properties After Heated: Thermosetting Plastic
• Plastic Forming Method: Extrusion
• Model NO.: MS245
• Color: White
• Transport Package: PP Bagag
• Specification: 800Kg
• Trademark: moresu
• Origin: China
• Production Capacity: 50000 Tons/Year

Product Description

                                             PA6 product introduction
Chinese name: Nylon 6
Aliases: Polyamide 6, Nylon 6, PA6           English Name: Polycaprolactam
Chemical formula: C6H13NO                    Molecular weight: 115.1735
Density: 1.13g/cm3
Appearance: Translucent or opaque milky white particles
Boiling point: 255°Cat760mmHg               Flash point: 102.2°C
Melting point: 215°C                        Shrinkage: 1%~1.5%
Relative value:2.42-2.47
Features: thermoplasticity, light weight, good toughness, chemical resistance and durability, etc.
Application: generally used in auto parts, mechanical parts, electronic appliances, engineering accessories, etc.

                                                  Product picture one                                                                                         Product picture two
Main application
Nylon yarn: widely used in clothing and textiles, such as cords, transmission belts, hoses, ropes, fishing nets, etc.
Engineering plastics: Filling glass fiber, carbon fiber, etc. can effectively increase the strength of the product, and it can be effectively used in industrial products. According to the application environment of different products, it can meet the characteristics of flame retardant, reinforcement, toughening, aging, weather resistance, etc. to meet product needs.
Sheets and bars: raw materials can be directly extruded.
Injection molding: widely used in gears, bearings, rollers, pulleys, cam nuts, gaskets, etc.



Characteristic:
The chemical and physical properties of nylon-6 are very similar to those of nylon 66. It has a lower melting point and a wide process temperature range. It has better impact and dissolution resistance than nylon 66 plastic, but is also more hygroscopic. Because many quality characteristics of plastic parts are affected by hygroscopicity, it is important to take this into account when designing products using nylon 6. In order to improve the mechanical properties of nylon 6, various modifiers are often added. Glass is the most common additive, and sometimes synthetic rubbers such as EPDM and SBR are added to improve impact resistance. For products without additives, the shrinkage of nylon 6 plastic material is between 1% and 1.5%. Adding glass fiber additives can reduce the shrinkage to 0.3% (but slightly higher in the direction perpendicular to the process). The shrinkage of molding assembly is mainly affected by the crystallinity and hygroscopicity of the material. Actual shrinkage is also a function of part design, wall thickness and other process parameters. Nylon 6 injection drying treatment Since nylon 6 easily absorbs moisture, special attention should be paid to the drying before processing. If the material is supplied in waterproof packaging, the container should be kept tightly closed. If the humidity is greater than 0.2%, it is recommended to dry in hot air above 80C for 16 hours. If the material has been exposed to air for more than 8 hours, vacuum drying at 105C for more than 8 hours is recommended. Nylon 6 injection molding process parameters Melt temperature: 240-250°C, 250-280°C for reinforced varieties.