PA6+30%Glasee Fiber, Ms1030g, Excellent Mechanical Properties, Dimensional Stability

• Fiberglass Type: Glass Fiber
• Certification: RoHS
• Technique: Compound
• Transport Package: Bags
• Specification: 25kg
• Trademark: moresu
• Model NO.: MS1030G
• Origin: China
• HS Code: 390810
• Production Capacity: 50000 Tons/Year

Product Description

Item	Test condition	Test standards	unit	Typicalvalue
Desity	23ºC	ISO 1183	g/m³	1.36
Molding shrinkage	flow	ISO 294-4	%	0.35-0.7
Melt Flow Rate	23ºC/ 50% r.h.	ISO 1133	g/10min	6.5
Tensile Strength at break	50 mm/min	ISO 527-2	Mpa	150
Elongation at break	5 mm/min	ISO 527-2	%	4
Cantilever notched impact strength	23ºC	ISO 180	kJ/m²	16
Flexural Strength	23ºC	ISO 178	Mpa	190
Flexural Modulus	23ºC	ISO 178	Mpa	7200
Melting temperature	DSC, 10ºC/min	ISO 11357-1	ºC	220
Temperature of deflection	1.80 Mpa	ISO 75-1,-2	ºC	210
Fire Resistance	1.6mm	UL94	Class	HB
GWIT	3.0mm	IEC 60695	ºC	750
GWFI	3.0mm	IEC 60695	ºC	960
CTI	Solution A	IEC 60112	V	250
Pre-drying temperature			ºC	90~110
Pre-drying time			h	3~4
Injection temperature			ºC	250~280
Mold temperature			ºC	80~100

 

30% fiberglass reinforced PA6 modified chips are ideal materials for processing power tool shells, power tool components, engineering machinery parts, and automotive parts. Their mechanical properties, dimensional stability, heat resistance, and aging resistance have been significantly improved, and their fatigue strength is 2.5 times that of unreinforced ones. The modification effect is the most obvious