Audited Supplier | Project | Inspection Standard | Test Conditions | test results |
| Relative viscosity | 2.83±0.05 | 2.83 | |
| Moisture content % | ≤0.06 | Karl Fischer method | 0.028 |
| Extract content % | ≤0.50 | hot water extraction | 0.28 |
| Mechanical properties | |||
| Tensile strength (mpa) | International | 20mm/min | 71.7 |
| elongation at break % | International | 20mm/min | 133 |
| tensile modulus (mpa) | International | 20mm/min | 1215 |
| flexural strength (mpa) | International | 5mm/min | 98.54 |
| flexural modulus (mpa) | International | 5mm/min | 2133.85 |
| notched impact strength (KJ/m2)
|
International | room temperature | 5.44 |
| thermal deformation temperature(ºC,1.82mpa) | International | 79.2 | |
| melt index (g/10min) test temperature 230ºC, Marfa weight 2160g, reaction time 10S; | International | 14.4 | |
| Shore hardness (HD) | International | 77.8 |