CAS No.: | 25038-54-4 |
---|---|
Formula: | (C6h11no)N |
EINECS: | 607-506-6 |
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Samples: |
---|
Suppliers with verified business licenses
Project | Inspection Standard | Test Conditions | test results |
Relative viscosity | 2.44±0.05 | 2.48 | |
Moisture content % | ≤0.06 | Karl Fischer method | 0.033 |
Extract content % | ≤0.50 | hot water extraction | 0.27 |
Mechanical properties | |||
Tensile strength (mpa) | International | 20mm/min | 76.6 |
elongation at break % | International | 20mm/min | 225.5 |
tensile modulus (mpa) | International | 20mm/min | 1226 |
flexural strength (mpa) | International | 5mm/min | 122.03 |
flexural modulus (mpa) | International | 5mm/min | 2951.13 |
notched impact strength (KJ/m2)
|
International | room temperature | 2.40 |
thermal deformation temperature(ºC,1.82mpa) | International | 53.2 | |
melt index (g/10min) test temperature 230ºC, Marfa weight 2160g, reaction time 10S; | International | 39.0 | |
Shore hardness (HD) | International | 84.0 |