Ultra Low Viscosity; Juheshun; J2000; Modified Binder, Spinning, PA6

• CAS No.: 25038-54-4
• Formula: (C6h11no)N
• EINECS: 607-506-6
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Model NO.: J2000
• Plastic Forming Method: Injection
• Color: White
• Transport Package: Bags
• Specification: 820kg
• Trademark: Juheshun
• Origin: China
• HS Code: 390810
• Production Capacity: 50000 Tons/Year

Product Description

Project	Inspection Standard	Test Conditions	test results
Relative viscosity	2.04±0.05		2.04
Moisture content %	≤0.06	Karl Fischer method	0.029
Extract content %	≤0.50	hot water extraction	0.14
Mechanical properties
Tensile strength (mpa)	International	20mm/min	68.2
elongation at break  %	International	20mm/min	34.9
tensile modulus  (mpa)	International	20mm/min	1228
flexural strength  (mpa)	International	5mm/min	120.41

flexural modulus  (mpa)	International	5mm/min	2886.74
notched impact strength  (KJ/m2)	International	room temperature	2.62
thermal deformation temperature(ºC,1.82mpa)	International		64.4
melt index (g/10min)   test temperature 230ºC, Marfa weight 2160g, reaction time 10S;	International		27.0
Shore hardness (HD)	International		83.0

The application of nylon in modification:
1. Nylon modification generally uses nylon resin chips with a viscosity of about 2.7, because this type of nylon raw material has excellent comprehensive performance and high cost performance.
2. If you want to choose a material with better fluidity, you can choose a nylon raw material with a viscosity below 2.5. The appearance of high-flow material products is better, especially when glass fiber or high-filling materials are added, such as making some larger products, such as : Engine cover, truck cooling fan, etc., or make some thin-walled or complex products, such as: micro-motor coil skeleton, large switch housing, etc.
3. If there are higher requirements for mechanical properties, high-viscosity nylon materials can be selected.